Fatigue Life of Welded and Bolted Repair Parts
Publication: Journal of Structural Engineering
Volume 110, Issue 10
Abstract
Fatigue crack propagation and residual stress measurement tests were conducted by using deep‐notched wide plate specimens with repaired parts. The main purpose of this study was to evaluate numerically the effects of some weld repair methods and a mechanically patching method with high strength grip bolts on residual fatigue life. The test results proved that the conventional welded repair method with no special treatment reduced fatigue life due to high tensile residual stress induced by welding repairs. However, through application of adequate treatment to cracks, compressive residual stress was induced in repair welds to increase the fatigue life. The remaining fatigue life of welded repair parts was further investigated using Fracture Mechanics. The patching method with high strength bolts and welded splice plates, on the other hand, had a remarkable effect on retarding the fatigue crack growth rate by decreasing it after bolted repairs to about 1/100‐1/1,000.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Abe, H., and Adachi, N., “Damage in Steel Bridges,” Structure Design Data, (Japan National Railway, No. 33, 197313, pp. 1396–1401.
2.
Abe, H., and Abe, M., “Fatigue of Floor System in Through Type Plate Girder Bridges (1st Report),” Structure Design Data, Japan National Railway, No. 60, 1972, pp. 1–5.
3.
Abe, H., and Abe, M., “Fatigue of Flood System in Through Type Plate Girder Bridges,” (2nd Report), Structure Design Data, Japan National Railway, No. 61, Jan., 1980, pp. 2–5.
4.
Abo, S., “Repair Examples of Steel Highway Bridges,” The Doboku Seko, Construction of Civil Engineering Structures, Vol. 20, No. 12, Nov., 1979, pp. 92–105.
5.
“ASCE Receives Grant to Set Up Structural Failure Center,” Engineering News Record, No. 13, Mar. 3, 1977.
6.
“Bridge Engineering,” Transportation Research Record 664, Vol. 1, 1978.
7.
“Crack, Weld Problems Shut Bridge,” Engineering News Record, No. 10, Sept. 15, 1977.
8.
“Cracked Girder Closes I‐79 Bridges,” Engineering News Record, No. 11, Feb. 10, 1977.
9.
“Crack Growth in Highway Girder Bridges,” Metal Construction, Sept., 1978, pp. 438–440.
10.
Dowrick, G., Cartwright, D. J., and Rook, D. P., “The Effects of Repair Patches on the Stress Distribution in a Cracked Sheet,” Numer. Methods Frac. Mech., 1980, pp. 763–775.
11.
Fisher, J. W., Barthelemy, B. M., Mertz, D. R., and Edinger, J. A., “Fatigue Damaged Bridges,” Transportation Research Record 664, 1978, pp. 102–109.
12.
Fisher, J. W., Barthelemy, B. M., Mertz, D. R., and Edinger, J. A., “Fatigue Behavior of Full‐scale Welded Bridge Attachments,” NCHRP Report No. 227, Transportation Research Board, Nov., 1980.
13.
Fisher, J. W., Frank, K. H., Hirt, M. A. M., and Mchamee, B. M., “Effect of Weldments on the Fatigue Strength of Steel Beams,” NCHRP Report 102, Highway Research Board, 1970.
14.
Gerberich, W. W., and Katz, Y., “On a Trigonometric Expression for the Single‐edge‐notch Specimen,” Eng. Frac. Mech., Vol. 1, 1969, pp. 569–570.
15.
Maas, G., “Investigation Concerning Craneway Girders,” Iron and Steel Engineering, Mar., 1972, pp. 49–58.
16.
Maeda, Y., Matsui, S., Kajikawa, Y., and Kawai, Y., “Structural Safety of Members in Highway Bridges Subjected to Repeated Loadings,” presented at the Dec., 1972, 19th Japan Bridge and Structural Engineering Symposium, held at Japan, pp. 79–88.
17.
Miki, C., Tajima, J., and Ashahi, K., “Fatigue of Large‐Size Partial Penetrated Longitudinal Butt Welds, Proceedings of JSCE, No. 322, June, 1982, pp. 143–156.
18.
Mori, T., and Horikawa, K., “Study on Fatigue Crack Growth Rate in Residual Stress Field (1st and 2nd Report),” presented at the Mar., 1982, Annual Conference of the Japan Welding Society (JWS), held at Japan, pp. 212–215, (Preprints).
19.
Nihei, K., “Study on Estimation of Fatigue Crack Propagation Life Taking Consideration into Residual Stress Due to Weld,” Report No. FS‐589‐82, Committee on Fatigue Strength of Welded Structures of the Japan Welding Society, May, 1982.
20.
Ohta, A., Sasaki, E., and Kosuge, M., “Effect of Mean Stress on Fatigue Crack Growth Rate,” Transactions, The Japan Society of Mechanical Engineers, Vol. 43, No. 373, pp. 3179–3191.
21.
Ohta, A., et al., “Fatigue Crack Growth Rate of Butt Welded Joints Under Several Stress Ratios,” Preprints, presented at the Mar. 1982, 30th Annual Conference of the Japan Welding Society, at Japan, pp. 216–217, (Preprints).
22.
“One in Six U.S. Highway Bridges is Deficient,” Engineering News Record, No. 19, Mar., 10, 1977, pp. 18–20.
23.
Paris, P. C., and Erdogan, F. E., “A Critical Analysis of Crack Propagation Laws,” Transactions, American Society of Civil Engineers, Vol. 85, Series D, No. 4, 1963, pp. 528–534.
24.
Reemsnyder, H. S., and Demo, D. A., “Fatigue Cracking in Welded Crane Runway Girders: Causes and Repair Procedures,” Iron and Steel Engineering, Apr., 1978, pp. 52–56.
25.
“Report on Fatigue Failure of Crane Girders,” Society of Steel Construction of Japan, Vol. 12, No. 128, Aug., 1976, pp. 9–22.
26.
Schwendeman, L. P., and Hedgren, A. W., Jr., “Bolted Repair of Fractured 1‐79 Girder,” Proceedings, American Society of Civil Engineers, Vol. 104, No. ST10, Oct., 1978.
27.
Senior, A. G., and Gurney, T. R., “The Design and Service Life of the Upper Part of Welded Crane Girders,” The Structural Engineer, No. 10 Vol. 41, Oct., 1963, pp. 301–312.
28.
“Standard Specifications for Highway Bridges,” AASHTO, 1977.
29.
Sweeney, R. A., “Some Examples of Detection and Repair of Fatigue Damage in Railway Bridge Members,” Transactions, Res. Rec., No. 676, 1978, pp. 8–14.
30.
Tanaka, K., “Fatigue Crack Property of Steel with Particular Reference to Threshold Stress Intensity Range, ,” Journal of the Iron and Steel Institute of Japan, Vol. 67, No. 2, 1981, pp. 245–253.
31.
Tanaka, K., “A Correlation of ‐value with the Exponent, m, in the Equation of Fatigue Crack Growth for Various Steels,” International Journal of Fracture, Vol. 15, No. 1, Feb., 1979, pp. 57–68.
32.
Tada, H., “A Note on the Finite Width Corrections to The Stress Intensity Factor,” Engineering Fracture Mechanics, Vol. 3, 1971, pp. 345–347.
33.
Umino, S., and Mimura, H., “Experimental Researches for Fractures in the Upper Flange of Welded Craneway Girders,” Transactions, The Architectural Institute of Japan, No. 318, Aug., 1982.
34.
Weymueller, C. R., “American Bridges Are in Trouble,” Welding Design & Fabrication, 1981, pp. 64–65.
35.
Wylde, J. G., and Booth, G. S., “Defect Assessment for Fatigue—The Techniques Described in PD 6493,” The Welding Bulletin, Apr., 1981, pp. 91–97.
36.
Wylde, J. G., “The Fatigue Performance of Repaired Fillet Welds,” Research Report No. 215/1983, The Welding Institute, May, 1983.
37.
Yagi, J., Tomita, J., Fujiki, Y., and Inoue, S., “Study on Fatigue Crack Growth Rate (2nd Report): Effect of Mean Stress,” Journal of the Society of Naval Architecture of Japan, No. 149, June, 1981, pp. 250–259.
38.
Yamasaki, T., and Kawai, Y., “Fatigue Design of Crane Runway Girders,” presented at the Sept., 1978 3rd International Symposium of Japan Welding Society, held at Tokyo, Japan, pp. 101–106.
Information & Authors
Information
Published In
Copyright
Copyright © 1984 ASCE.
History
Published online: Oct 1, 1984
Published in print: Oct 1984
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.