Dislocation Emission Model of Kinked Cracks in Aluminum Crystal under the Condition of Hydrogen Filling
Publication: Journal of Engineering Mechanics
Volume 150, Issue 12
Abstract
Based on the method of continuous distribution of dislocations and relevant theories of fracture mechanics, the effect of the distribution of hydrogen atoms at the crack tip (CT) on the emission of dislocations from kinked cracks under far-field uniform tensile stress is studied. The results show that hydrogen atoms can promote the emission and migration of CT dislocation, which leads to the increase of dislocation density (severe dislocation plugging), the increase of energy release rate, and the decrease of elastic zone size (dislocation-free zone) at CT. In addition, the sequence of initiation of grain boundary (GB) microcracks caused by dislocation emission at both ends of the whole crack (horizontal section and kinked section) and the propagation mechanism of a crack in a kinked section are analyzed. The results show that the critical tensile stress of GB microcrack initiation decreases with the increase of hydrogen atom radius and the decrease of hydrogen atom position , indicating that hydrogen atoms promote the initiation of GB microcrack initiation. At the same time, the existence of hydrogen atoms not only promotes the initiation of GB microcrack, but also accelerates the expansion of kinked cracks, which may eventually lead to the convergence of the main crack and the microcrack, resulting in the failure and destruction of materials. Therefore, the theoretical research in this paper has made a new understanding of the mechanism of hydrogen fracture of crystal materials.
Practical Applications
In this paper, the effects of hydrogen atoms at CT on dislocation emission at CT, crack initiation at GB, and the size of the dislocation-free zone were studied by establishing a crack dislocation model and using the distributed dislocation method. The results show that the accumulation of hydrogen atoms at the CT promotes the emission of dislocation at the CT, leads to the serious plugging of dislocation near the GB, promotes the initiation of microcracks and the expansion of kinked cracks, and leads to the reduction of the size of the dislocation-free zone at the CT. This work provides new information on the microscopic fracture mechanics of hydrogen on materials. On the one hand, it can better predict and prevent the fracture of materials, so as to improve the safety of engineering structures. On the other hand, it can help explain some microscopic experimental phenomena.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code generated or used during the study are proprietary or confidential in nature and may only be provided with restrictions.
Acknowledgments
This work was supported by the National Natural Science Foundation of China (Grant No. 11472230).
Author contributions: Keke Zhao: conceptualization, methodology, investigation, and writing–original draft. Hongda Yang: methodology and investigation. Jiding Zhang: investigation and methodology. Yundie Zhu: methodology and investigation. Xiaoyu Jiang: writing–review and editing.
References
Amp, N. K., and H. Vehoff. 2012. “Novel methods for micromechanical examination of hydrogen and grain boundary effects on dislocations.” Philos. Mag. 92 (25–27): 3216–3230. https://doi.org/10.1080/14786435.2012.690939.
Birnbaum, H. K., and P. Sofronis. 1994. “Hydrogen-enhanced localized plasticity—A mechanism for hydrogen-related fracture.” Mater. Sci. Eng. A 176 (1–2): 191–202. https://doi.org/10.1016/0921-5093(94)90975-X.
Bond, G. M., I. M. Robertson, and H. K. Birnbaum. 1988. “Effects of hydrogen on deformation and fracture processes in high-ourity aluminium.” Acta Metall. 36 (8): 2193–2197. https://doi.org/10.1016/0001-6160(88)90320-3.
Cotterll, A. H., and B. A. Bilby. 1949. “Dislocation theory of yielding and strain ageing of iron.” Proc. Phys. Soc. Sect. A 62 (1): 49–62. https://doi.org/10.1088/0370-1298/62/1/308.
Dietzel, W. 2012. Gaseous hydrogen embrittlement of materials in energy technologies, 237–273. Sawston, UK: Woodhead.
Domizzi, G., G. Anteri, and J. Ovejero-Garcia. 2001. “Influence of sulphur content and inclusion distribution on the hydrogen induced blister cracking in pressure vessel and pipeline steels.” Corros. Sci. 43 (2): 325–339. https://doi.org/10.1016/S0010-938X(00)00084-6.
Du, Y., X. Gao, and L. Lan. 2019. “Hydrogen embrittlement behavior of high strength low carbon medium manganese steel under different heat treatments.” Int. J. Hydrogen Energy 44 (60): 32292–32306. https://doi.org/10.1016/j.ijhydene.2019.10.103.
Gao, X. 2005. “Displacement burst and hydrogen effect during loading and holding in nanoindentation of an iron single crystal.” Scr. Mater. 53 (11): 1315–1320. https://doi.org/10.1016/j.scriptamat.2005.06.042.
Hills, D., P. Kelly, D. Dai, and A. Korsunsky. 1996. Solution of crack problems: The distributed dislocation technique. Dordrecht, Netherlands: Kluwer Academic.
Ko, W. S., J. B. Jeon, and J. H. Shim. 2012. “Origin of hydrogen embrittlement in vanadium-based hydrogen separation membranes.” Int. J. Hydrogen Energy 37 (18): 13583–13593. https://doi.org/10.1016/j.ijhydene.2012.06.075.
Kumar, K. S., S. Suresh, and M. F. Chisholm. 2003. “Deformation of electrodeposited nanocrystalline nickel.” Acta Mater. 51 (2): 387–405. https://doi.org/10.1016/S1359-6454(02)00421-4.
Li, X., X. Jiang, and X. Li. 2016. “Solution of an inclined crack in a finite plane and a new criterion to predict fatigue crack propagation.” Int. J. Mech. Sci. 119 (Dec): 217–223. https://doi.org/10.1016/j.ijmecsci.2016.10.019.
Li, X., A. G. Sheinerman, and H. Yang. 2022. “Theoretical modeling of toughening mechanisms in the CrMnFeCoNi high-entropy alloy at room temperature.” Int. J. Plast. 154 (Jul): 103304. https://doi.org/10.1016/j.ijplas.2022.103304.
Li, X. J. X. 2019. “Theoretical analyses of nanocrack nucleation near the main crack tip in na-no and micro crystalline materials.” Eng. Fract. Mech. 221 (Nov): 106672. https://doi.org/10.1016/j.engfracmech.2019.106672.
Liu, H. W. 2011. “Hydrogen assisted intergranular cracking in steels.” Eng. Fract. Mech. 78 (14): 2563–2571. https://doi.org/10.1016/j.engfracmech.2011.06.019.
Lynch, S. P. 2013. “Mechanisms and kinetics of environmentally assisted cracking: Current status, issues, and suggestions for further work.” Metall. Mater. Trans. A 44 (3): 1209–1229. https://doi.org/10.1007/s11661-012-1359-2.
Nair, S. V., R. R. Jensen, and J. K. Tien. 1983. “Kinetic enrichment of hydrogen at interfaces and voids by dislocation sweep-in of hydrogen.” Metall. Trans. A 14 (2): 385–393. https://doi.org/10.1007/BF02644216.
Nuismer, R. J. 1975. “An energy release rate criterion for mixed mode fracture.” Int. J. Fract. 11 (2): 245–250. https://doi.org/10.1007/BF00038891.
Ovid’ko, I. A., A. G. Sheinerman, and E. C. Aifantis. 2008. “Stress-driven migration of grain boundaries and fracture processes in nanocrystalline ceramics and metals.” Acta Mater. 56 (12): 2718–2727. https://doi.org/10.1016/j.actamat.2008.02.004.
Sofronis, P., and I. M. Robertson. 2002. “Transmission electron microscopy observations and micromechanical/continuum models for the effect of hydrogen on the mechanical behaviour of metals.” Philos. Mag. A 82 (17–18): 3405–3413. https://doi.org/10.1080/01418610208240451.
Takahashi, Y., H. Kondo, and R. Asano. 2016. “Direct evaluation of grain boundary hydrogen embrittlement: A micro-mechanical approach.” Mater. Sci. Eng. A 661 (Apr): 211–216. https://doi.org/10.1016/j.msea.2016.03.035.
Tehranchi, A., and W. A. Curtin. 2017. “Atomistic study of hydrogen embrittlement of grain boundaries in nickel: I. Fracture.” J. Mech. Phys. Solids 101 (Apr): 150–165. https://doi.org/10.1016/j.jmps.2017.01.020.
Tomatsu, K., H. Kawata, and T. Amino. 2017. “In-situ microbending tests of Ni-Cr alloy during cathodic hydrogen charging by electrochemical nanoindentation.” ISIJ Int. 57 (Apr): 564–572. https://doi.org/10.2355/isijinternational.ISIJINT-2016-540.
Troiano, A. R. 2016. “The role of hydrogen and other interstitials in the mechanical behavior of metals.” Metallogr. Microstruct. Anal. 5 (6): 557–569. https://doi.org/10.1007/s13632-016-0319-4.
Ven, A. V. D., and G. Ceder. 2004. “The thermodynamics of decohesion.” Acta Mater. 52 (5): 1223–1235. https://doi.org/10.1016/j.actamat.2003.11.007.
Wei, Y. J., and L. Anand. 2004. “Grain-boundary sliding and separation in polycrystalline metals: Application to nanocrystalline FCC metals.” J. Mech. Phys. Solids 52 (11): 2587–2616. https://doi.org/10.1016/j.jmps.2004.04.006.
Yokobori, A. T. 2004. “The mechanism of hydrogen embrittlement: The stress interaction between a crack, a hydrogen cluster, and moving dislocations.” Int. J. Fract. 128 (1–4): 121–131. https://doi.org/10.1023/B:FRAC.0000040974.59017.55.
Zhang, J., Y. Sheng, and H. Yang. 2022. “Crystal crack dislocation model in the hydrogen environment.” Eng. Fract. Mech. 270 (Jul): 108587. https://doi.org/10.1016/j.engfracmech.2022.108587.
Zheng, J. Y., X. X. Liu, and P. Xu. 2012. “Development of high pressure gaseous hydrogen storage technologies.” Int. J. Hydrogen Energy 37 (5): 1048. https://doi.org/10.1016/j.ijhydene.2011.02.125.
Information & Authors
Information
Published In
Copyright
© 2024 American Society of Civil Engineers.
History
Received: Jan 19, 2024
Accepted: Jul 19, 2024
Published online: Sep 24, 2024
Published in print: Dec 1, 2024
Discussion open until: Feb 24, 2025
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.